MegaPro Epo Y502 | Epoxy Based Adhesive
Please click on "Offer Request" button below to send your offer and detailed information request to the company for the MegaPro Epo Y502 | Epoxy Based Adhesive product.
MegaPro Epo Y502 is used in reinforcement works to ensure adhesion of MegaKarbon Plate K919 to the surface of the construction elements.
Performance
• Density (kg/lt) 2,00±0,10
• Drying Period (@23 °C, %55 RH) (Hour) 8±1
• Full Hardening (@23 °C, %55 RH) (Week) 1
• Compressive Strength (MPa) >40
• Sliding Strength (MPa) >6
• Modulus of Elasticity (MPa) >2600
• Tensile Adhesive Strength (MPa) %100 concrete rapture
• Sliding Strength >6
• Coefficient of Thermal Expansion < 100 x 10-6 /K
• Glass Transition Temperature (˚C) > 40
Application Limits
• Period of use of the prepared mixture – Pot Life: 60 minutes
• Drying Period: 8±1 hours
• Full Cure: 7 days
These values are obtained under laboratory conditions, from tests performed at 23 ± 2°C and %50 ± 5 relative humidity. The values may vary according to the surface and ambient conditions.
Technicial Specifications
• Chemical Structure: Epoxy based adhesive
• Density: 2 kg/lt
• Color: Gray
Mixing Ratio
• A and B components must be fully mixed.
Consumption
• The consumption amount for concrete surfaces is 2-3 kg/m2. This number varies according to the surface and ambient conditions.
Packaging
• MegaPro Epo Y502 is supplied in net 6 kg (Component A: 3 kg; Component B: 3 kg) containers as a set.