MegaPro Epo Y501 | Epoxy Based Adhesive
Please click on "Offer Request" button below to send your offer and detailed information request to the company for the MegaPro Epo Y501 | Epoxy Based Adhesive product.
MegaPro Epo Y501 is used in reinforcement works to ensure adhesion of MegaKarbon Wrap 300 K918 to the surface of the construction elements.
Performance
• Density (kg/lt): 1,08
• Pot Life (@23°C) (Minutes): 60
• Drying Period (@23°C) (Hours): 10
• Full Hardening (@23°C) (Weeks): 1
• Compressive Strength (MPa): 79
• Sliding Strength (MPa): >6
• Tensile Adhesive Strength (MPa): 52
These values are obtained under laboratory conditions, from tests performed at 23 ± 2°C and %50 ± 5 relative humidity. The values may vary according to the surface and ambient conditions.
Application Limits
• Period of use of the prepared mixture – Pot Life: 60 minutes
• Drying Period: 10 hours
• Full Cure: 7 days
These values are obtained under laboratory conditions, from tests performed at 23 ± 2°C and %50 ± 5 relative humidity. The values may vary according to the surface and ambient conditions.
Technicial Specifications
• Chemical Structure: Epoxy based lamination resin
• Density: 1,08 kg/lt
• Color: Blue
Mixing Ratio
• A and B components must be fully mixed.
Consumption
• The product is applied as primer and first coat with a consumption of 1.0-1.5 kg/m2 on concrete surfaces. MegaKarbon Wrap 300 K918 is saturated with MegaPro Epo Y501 with a jagged roller after the application of the first coat. The consumption for any subsequent coating is approximately 0.4-0.6 kg/m2. This value may vary according to the surface and ambient condition.